Chemical Composition

Grade Symbol	UNS Number	Alloy	Elements	Composition %
F316L	S31603	18 chromium, 8 nickel, modified with molybdenum, low carbon 316LG	Carbon	0.030 max
			Manganese	2.00 max
			Phosphorus	0.045 max
			Sulfur	0.030 max
			Silicon	1.00 max
			Nickel	10.0–15.0
			Chromium	16.0–18.0
			Molybdenum	2.00–3.00
			Nitrogen	0.10

Mechanical Properties

Property	Value
Tensile Strength, min, ksi [MPa]	70 [485]
Yield Strength, min, ksi [MPa]	25 [170]
Elongation in 2 in. [50mm] or 4D, min, %	30
Reduction or Area, min, %	50

Heat Treatment

After hot working, forgings shall be cooled to a temperature below 1000 °F [538 °C] prior to heat treating in accordance with the requirements.